Implementing All-Weather Photocatalysis of Exhaust Fumes Based on the g-C3N4/TiO2/SrAl2O4: Eu2+, Dy3+ Ternary Composite Coating

This study examines the use of SrAl2O4: Eu2+, Dy3+ long-afterglow materials doped into g-C3N4/TiO2 coatings for photodegradation. The prepared sample was tested for the purification of automotive exhaust fumes, with the optimal mass ratio of g-C3N4/TiO2 and SrAl2O4: Eu2+, Dy3+ determined to be 1:1. Characterization tests, including XRD, FT-IR, XPS, and TG-DSC, were conducted to evaluate the microstructure and properties of the samples. Under poor lighting conditions, g-C3N4/TiO2 reduced CH and NOx by 59 ppm and 13 ppm within 4 h, respectively, while g-C3N4/TiO2/SrAl2O4: Eu2+, Dy3+ decreased CH and NOx by 98ppm and 34ppm, respectively, resulting in a significant improvement in degradation efficiency. The addition of long-afterglow materials significantly improves the efficiency of photocatalysts in purifying exhaust fumes in low-light environments, providing potential value for all-weather exhaust treatment in the future.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.