Implementing All-Weather Photocatalysis of Exhaust Fumes Based on the g-C3N4/TiO2/SrAl2O4: Eu2+, Dy3+ Ternary Composite Coating
Autor(en): |
Bochao Zhou
Hailong Li Ao Cui Di Wang Fucheng Guo Chao Wang |
---|---|
Medium: | Fachartikel |
Sprache(n): | Englisch |
Veröffentlicht in: | Buildings, 19 Juni 2024, n. 6, v. 14 |
Seite(n): | 1743 |
DOI: | 10.3390/buildings14061743 |
Abstrakt: |
This study examines the use of SrAl2O4: Eu2+, Dy3+ long-afterglow materials doped into g-C3N4/TiO2 coatings for photodegradation. The prepared sample was tested for the purification of automotive exhaust fumes, with the optimal mass ratio of g-C3N4/TiO2 and SrAl2O4: Eu2+, Dy3+ determined to be 1:1. Characterization tests, including XRD, FT-IR, XPS, and TG-DSC, were conducted to evaluate the microstructure and properties of the samples. Under poor lighting conditions, g-C3N4/TiO2 reduced CH and NOx by 59 ppm and 13 ppm within 4 h, respectively, while g-C3N4/TiO2/SrAl2O4: Eu2+, Dy3+ decreased CH and NOx by 98ppm and 34ppm, respectively, resulting in a significant improvement in degradation efficiency. The addition of long-afterglow materials significantly improves the efficiency of photocatalysts in purifying exhaust fumes in low-light environments, providing potential value for all-weather exhaust treatment in the future. |
Copyright: | © 2024 by the authors; licensee MDPI, Basel, Switzerland. |
Lizenz: | Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden. |
4.06 MB
- Über diese
Datenseite - Reference-ID
10787605 - Veröffentlicht am:
20.06.2024 - Geändert am:
20.06.2024