Study of Low-Content Epoxy Asphalt Mixture Applied to the Road

To realize the application of epoxy asphalt concrete on roads and solve the problem of the high cost of epoxy asphalt concrete and the causes of bulging in the construction process, a low-content epoxy asphalt mixture was experimentally studied. Rheological and microscopic tests were carried out to study its performance. At the same time, 17 kinds of low-content asphalt mixture Marshall test pieces and rut plate test pieces with different oil stone ratios were made. Their road performances were tested, and a watertight breathable epoxy asphalt mixture was studied to solve the bulging problem. The research shows that, for ordinary roads, a content of epoxy resin of 10–15% can meet both the high-temperature and the low-temperature requirements. For sections with special rutting resistance requirements, a controlled epoxy resin content between 15 and 30% is recommended. When the content of epoxy resin is greater than 30%, epoxy asphalt initially forms a crosslinked spatial network. An epoxy asphalt with a complex structure from asphaltene to epoxy, with ultra-high performance, can be used for small steel bridge pavements. A BBR test showed that, with an increase in epoxy resin content, the low-temperature performance of asphalt gradually weakens. When the content was 20%, epoxy asphalt’s low-temperature performance was weaker than that of SBS-modified asphalt. Under extremely low-temperature conditions, the performance of epoxy asphalt could not meet the specifications. When the voids of low equivalent epoxy asphalt mixture are controlled at 4.1–4.5%, it is watertight and breathable; this can solve the problem of bulging and greatly reduce the cost of projects.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.