Development of Wood-Crete from Hardwood and Softwood Sawdust

Wood-crete, a new building material has previously been developed from sawdust, inorganic binder and addition of waste paper, finding its use mainly for wall panelling or other non- and semi-structural applications with good thermal insulating properties.

In this study, the properties of wood-crete were investigated based on the type of wood sawdust – hardwood (beech and oak) and softwood (pine and cedar). The results showed that (1) the compressive strength of wood-crete was closely related to the wood species, with the compressive strength of 3.93MPa being for hardwood wood-crete compared to 1.37MPa and 0.26MPa of wood-crete from softwood and mixed wood respectively; (2) wood-crete from hardwood sawdust had a higher density than those made from softwood sawdust and mixed wood; (3) particle size had a significant influence on the strength properties and density of wood-crete with wood-crete made from 1mm particle size recording a higher compressive strength and density compared to 2mm and 3mm particle size. The optimum size for wood-crete was dependent on the wood species; (4) thermal conductivity of wood-crete was closely related to the chemical composition of various wood species, with softwood wood-crete having about 20% lower thermal conductivity compared to hardwood wood-crete; (5) a ratio of 1:2 of sawdust to binder was found advisable for the production of wood-crete for various wood species and particle sizes investigated. The compressive strength of wood-crete made from sawdust of both softwood and hardwood was similar to or higher than that of hempcrete, indicating their suitability for wall panelling or other non- and semi-structural applications. The results of this study provide an important foundation for choosing what wood species, particle sizes and combinations of sawdust to be used for the production of wood-crete.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.