Study on Mechanical Properties and Durability of Alkali-Activated Silicomanganese Slag Concrete (AASSC)

Alkali-activated materials are produced by chemically polymerizing the aluminosilicate materials using alkaline activators, which can effectively lower the greenhouse-gas emissions (approximately 73%) released by ordinary Portland cement (OPC). Silicomanganese slag is a large solid waste discharged from the ferroalloy industry in China that can pollute the environment and occupy resources. In this paper, the slag in alkali-activated material was replaced with silicomanganese slag to address the disposal of silicomangaese slag. The flowability, setting times, compressive and flexural strengths, micro-structure and freeze-thaw resistance of alkali-activated silicomanganese slag concrete (AASSC) with varied substitution ratios, volume fractions of steel fibers and alkali-activated modulus (MS) were exploited. As a results the compressive strengths at 56 days of AASSC with a 10% substitution ratio of silicomanganese slag reached over 80 MPa and over 132 MPa with the 3% steel fiber dosage. AASSC still reached 91 MPa and 45 MPa with 60% and 100% substitution ratios by cooperating 2% steel fibers, respectively. When the freeze-thaw cycle number reached 300, the compressive strengths of AASSC with the replacement ratios of 10%, 60% and 100% were 84%, 74% and 51% of their original values by cooperating 2% steel fibers, respectively; AASSC with the numerous substitutions of 60% and 100% were destroyed at 600 and 300 freeze-thaw cycles, respectively. AASSC with a 10% substitution ratio and 2% steel fiber content is suitable for excellent performance, and a 60% substitution ratio can also be applied to construction for the massive utilization of silicomanganese slag.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.