Strength Design of Ultra-High-Performance Fiber-Reinforced Cementitious Composites Using Local Ecological Admixture

The ultra-high-performance fiber-reinforced cementitious composite (UHPFRC) is a new generation of building material with extremely high mechanical strength and durability, which can be used for ultra-high, thin-wall or long-span construction, that prolongs the service life of construction in severe environments. In this study, UHPFRC was prepared with a high range of local ecological admixture to decrease the material’s cost and the environmental impact. Raw materials’ proportions, water/binder ratio, fiber-volume contents, and hybrid-fiber ratio were studied on the property improvement of UHPFRC, and an F-test analysis was induced to reveal the important significance on compressive strength. The results demonstrated that the compressive strength of 237.8 MPa was achieved with mineral admixture substitution over 40%. The particle_packing density and the binder reactivity both succeeded on the compressive strength. Water/binder ratio determined the hydration degree and the flowability of UHPFRC, which affected compressive strength through hydration products and microstructure. Also, compressive strength was more sensitive with hybrid-fiber than fiber-volume content. The order of importance for compressive strength was powder proportion > hybrid-fiber ratio > fiber-volume content > water/binder ratio.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.