Post-Fire Mechanical Properties of Half-Grouted Sleeve Connectors with Grouting Defects

Half-grouted sleeve connectors are a primary method for connecting rebar in prefabricated concrete structures. However, due to limitations in the construction environment, all kinds of grouting defects are inevitable, especially grouting voids. Additionally, fire disasters, among the most common types of disasters, significantly threaten the structural performance and safety of these prefabricated structures. Therefore, it is imperative to determine the mechanical properties of half-grouted sleeve connectors with grouting voids after high temperatures. This study designed and prepared 48 groups of half-grouted sleeve specimens with different grouting voids and defect locations. These specimens were heated to the specified temperature (25 °C, 200 °C, 300 °C, 400 °C, 500 °C, 600 °C), followed by unidirectional tensile testing after natural cooling. The experimental results showed that rebar fracture failure and rebar pulled-out failure were the failure modes of specimens. With the increase in temperature, bearing capacity, safety factor and ductility coefficient of specimens all decreased. When the temperature was lower than 400 °C, the specimen with void length less than twice the diameter of the rebar (i.e., 2d) had sufficient connection performance. For specimens with the same total void lengths, the bearing capacity of discrete voids is lower than concentrate voids at the same temperature. The load-displacement curve, safety coefficient, ductility coefficient and grey correlation degree of half-grouted sleeve specimens with grouting voids at different temperatures are analyzed and discussed, and the bond stress slip constitutive model is given. Grouting defects have greater influence on specimens after grey correlation analysis. Findings from this study provide valuable references for the safety performance evaluation of prefabricated structures with half-grouted sleeve connectors after exposure to fire.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.