A Low-Carbon Composite Cementitious Material Manufactured by a Combined Process of Red Mud

In present study, the effects of varying dosages of combined red mud on the microstructure and hydration process of low-carbon composite cementitious material. The findings indicated a gradual decrease in the reactivity of RM, following a linear trend. The non-evaporable water content of the composite binder exhibited an initial increase followed by a subsequent decrease, with the optimal content identified at 10%, for RM content ranging from 10% to 90%, non-evaporable water decreases linearly. Optimal bending strength and compressive strength were achieved in the mortar when incorporating 10% of RM, reaching 8.56 MPa and 51.2 MPa at 28 days, respectively. The porosity was at its lowest when the RM content was added at 10%, but further increasing RM dosage was reversed. The pore size distribution aligned with the experimental findings on porosity. X-ray diffraction (XRD) analysis revealed the involvement of RM in the secondary hydration reaction, thereby enhancing the mechanical properties of low-carbon composite cementitious material. The optimal content of RM is suggested to be 10%, with a maximum recommended limit of 30%. The analysis has shown that red mud particles serve a dual purpose in low-carbon composite cementitious material. They enhance compactness by acting as fillers and promote cement hydration through surface activity, thereby enhancing mechanical properties, durability, and pore size distribution.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.