The Influence of Physical Activation of Portland Cement in the Electromagnetic Vortex Layer on the Structure Formation of Cement Stone: The Effect of Extended Storage Period and Carbon Nanotubes Modification

The article presents research of the influence of the electromagnetic vortex layer on the structure formation of cement stone during the activation of portland cement, both without additives and with carbon nanotubes modification. It has been shown that the storage of portland cement powders in open air for 60 days after activation in the electromagnetic mill leads to partial carbonization, wherein the role in absorption reducing of the super plasticizer additive is increased since there is more uniformly localization of the additive on the surface of the portland cement particles. The processing of portland cement in the electromagnetic mill leads to the physical activation of portland cement, which is accompanied by an increase in the amount of heat generated by the hydration of portland cement and the rate of hydration. Thus, the rate of hydration of compositions activated in the electromagnetic mill isincreased 1.615 times at the temperature of the thermostat 22 °C; 1.85 times at 40 °C; 2.71 times at 60 °C; 2.3 times at 80 °C. The modification of cement stonewith carbon nanotubes, which was obtained from portland cement activated in an electromagnetic mill, leads to a higher quantity of silicate phase of portland cement (by 12–39%), as confirmed by a decrease in the number of portlandite in these compositions by 8% in comparison with control composition.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.