Cyclic Void Growth Model Parameter Calibration of Q460D Steel and ER55-G Welds after Exposure to High Temperatures

When high-strength steel is heated to high temperatures and then cooled naturally, its ductility decreases. In earthquake-prone areas, it is necessary to evaluate the ultra-low cycle fatigue fracture (ULCF) behavior of high-strength steel structures after a fire if these structures are used continuously. However, the ULCF fracture model of high-strength steel subjected to high temperatures followed by natural cooling has not been deeply studied. In view of this, twelve notched, round bar specimens fabricated from Q460D steel and ER55-G welds were heated to 900 °C followed by natural cooling and then cyclic loading experiments and finite element analyses (FEA) were performed on these specimens. The fracture deformation obtained from the experiments was used in the FEA to calibrate the damage degradation parameter of a Cyclic Void Growth Model (CVGM) of Q460D steel and ER55-G welds under this condition. The calibrated values were 0.30 and 0.20, respectively. The calibrated CVGM was employed to predict the number of cycles and the force and displacement at the fracture moment of the notched round bar specimens. The predicted results aligned closely with the experimental results, indicating that CVGM is effective in predicting the fracture of Q460D steel and ER55-G welds following exposure to 900 °C and subsequent natural cooling.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.