Bond Behavior of Carbon Fabric-Reinforced Matrix Composites: Geopolymeric Matrix versus Cementitious Mortar

This study aims to examine the potential use of a geopolymeric matrix as a sustainable alternative to commercial mortars in carbon fabric-reinforced matrix composites. Single-lap shear tests were conducted to examine the bond behavior at the fabric-matrix interface. Test parameters included the type of matrix (geopolymeric and cementitious matrices) and the bonded length (50 to 300 mm). The geopolymeric matrix was a blend of fly ash/ground granulated blast furnace slag activated by an alkaline solution of sodium silicate and sodium hydroxide. The bond behavior of the geopolymeric-matrix specimens was characterized and compared to that of similar specimens with a cementitious matrix. The specimens failed due to fabric slippage/debonding at the fabric-matrix interface or fabric rupture. The effective bond lengths of the geopolymeric- and cementitious-matrix specimens were 150 and 170 mm, respectively. The geopolymeric-matrix specimens exhibited higher fabric strains, higher ultimate loads, and a steeper strain profile along the bonded length than those of their cementitious-matrix counterparts. New bond-slip models that characterize the bond behavior at the fabric-matrix interface for geopolymeric- and cementitious-matrix specimens were developed. Both models exhibited equal maximum shear stress of 1.2 MPa. The geopolymeric-matrix model had, however, higher fracture energy and higher slip at maximum shear stress than those of the cementitious matrix model.

This creative work has been published under the Creative Commons Attribution 4.0 International (CC-BY 4.0) license which allows copying, and redistribution as well as adaptation of the original work provided appropriate credit is given to the original author and the conditions of the license are met.