Workability of Nanomodified Self-Compacting Geopolymer Concrete Based on Response Surface Method

Geopolymer concrete is more low-carbon and environmentally friendly than Portland cement concrete. Nanoparticle modification can help to improve the mechanical and durability performance of concrete, but due to its large specific surface area and high activity, it may deteriorate its workability. However, there is currently limited research on the effect of nanomodification on the workability of freshly mixed self-compacting geopolymer concrete (SCGC). This article conducted SCGC workability experiments using the response surface methodology, which included 29 different mixtures. The effects of nano-silica (NS), nano-calcium carbonate (NC), alkali content (N/B), and water cement ratio (W/B) on the workability of SCGC were studied. The experimental results show that the addition of NS and NC can reduce the slump expansion of SCGC, and the combination of the two significantly increases the amplitude of slump expansion with the change in nanomaterial content. An increase in N/B will reduce the expansion time and clearance value of SCGC. As N/B increases from 4% to 4.4%, the slump extension of SCGC decreases, and with a further increase in N/B, the slump extension increases significantly to 68.1 cm, which means that the slump extension of SCGC increases by 9.5% as N/B increases from 4.4 to 5. This study can provide a reference for optimizing the fresh performance of geopolymer concrete and improving the mechanism of nanomaterial-modified geopolymer concrete.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.