The Properties of Magnesium Silicate Hydrate Prepared from the Magnesium Silicate Minerals in the Earth’s Crust

In order to explore a wider range and lower cost of raw materials for the preparation of magnesium silicate hydrate (M-S-H), an acid-leaching method was employed to extract and separate high-purity magnesium hydroxide (Mg(OH)2) with a purity higher than 97% and amorphous silica with a purity higher than 90% from four types of natural silicate minerals (serpentine, peridotite, zeolite, and montmorillonite). These two intermediate products, which are amorphous silica and magnesium hydroxide, were used to prepare M-S-H, and the influence of curing at two temperatures, 50 °C and 80 °C, on the properties of M-S-H was investigated. The results showed that with the increase in curing temperature, the bound water content, tetrahedral polymerization degree, and Mg(OH)2 content increased. There was a good correlation between the increase in strength and the bound water content of M-S-H. This work provides a possible technological route for expanding the raw materials for preparing magnesium silicate hydrate cementitious materials and utilizing the abundant magnesium silicate minerals in the Earth’s crust.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.