The Properties of Magnesium Silicate Hydrate Prepared from the Magnesium Silicate Minerals in the Earth’s Crust

In order to explore a wider range and lower cost of raw materials for the preparation of magnesium silicate hydrate (M-S-H), an acid-leaching method was employed to extract and separate high-purity magnesium hydroxide (Mg(OH)2) with a purity higher than 97% and amorphous silica with a purity higher than 90% from four types of natural silicate minerals (serpentine, peridotite, zeolite, and montmorillonite). These two intermediate products, which are amorphous silica and magnesium hydroxide, were used to prepare M-S-H, and the influence of curing at two temperatures, 50 °C and 80 °C, on the properties of M-S-H was investigated. The results showed that with the increase in curing temperature, the bound water content, tetrahedral polymerization degree, and Mg(OH)2 content increased. There was a good correlation between the increase in strength and the bound water content of M-S-H. This work provides a possible technological route for expanding the raw materials for preparing magnesium silicate hydrate cementitious materials and utilizing the abundant magnesium silicate minerals in the Earth’s crust.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.