Evaluating Iraqi Modified Asphalt Concrete Moisture Resistance Based on Strength Ratio and Fracture Energy Parameters

Auteur(s):


Médium: article de revue
Langue(s): anglais
Publié dans: Advances in Civil Engineering, , v. 2019
Page(s): 1-7
DOI: 10.1155/2019/8521682
Abstrait:

Two types of polymers (plastomer (functionalized polyethylene (PE)) and elastomer (styrene-butadiene-styrene (SBS))) were used for shifting up asphalt binder performance grade (PG) and tensile strength resistance (moisture damage) of the asphalt concrete mixture. It is found that adding 3.5% functionalized polyethylene (PE) polymer to the binder is more effective than adding 4% styrene-butadiene-styrene (SBS) to shift up asphalt PG by two grades to PG 76-16. Furthermore, the viscosity of the binder increased about 200% when using 4% SBS, while there is no significant effect on viscosity when 3.5% PE is used. Therefore, there is no need to increase the temperature of mixing and compaction which may affect polymers. The indirect tensile test was used for measuring tensile strength ratio of dry and wet samples (conditioned according to ASTM D4867) and found that this ratio increased by 10 to 18% when using 4% SBS and 3.5% PE, respectively. Fracture energy (area under the strength-strain curve) and elasticity were estimated for neat and modified mixture samples.

Copyright: © 2019 Hasan Al-Mosawe et al.
License:

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.

  • Informations
    sur cette fiche
  • Reference-ID
    10315401
  • Publié(e) le:
    28.06.2019
  • Modifié(e) le:
    02.06.2021