Evaluating Iraqi Modified Asphalt Concrete Moisture Resistance Based on Strength Ratio and Fracture Energy Parameters

Two types of polymers (plastomer (functionalized polyethylene (PE)) and elastomer (styrene-butadiene-styrene (SBS))) were used for shifting up asphalt binder performance grade (PG) and tensile strength resistance (moisture damage) of the asphalt concrete mixture. It is found that adding 3.5% functionalized polyethylene (PE) polymer to the binder is more effective than adding 4% styrene-butadiene-styrene (SBS) to shift up asphalt PG by two grades to PG 76-16. Furthermore, the viscosity of the binder increased about 200% when using 4% SBS, while there is no significant effect on viscosity when 3.5% PE is used. Therefore, there is no need to increase the temperature of mixing and compaction which may affect polymers. The indirect tensile test was used for measuring tensile strength ratio of dry and wet samples (conditioned according to ASTM D4867) and found that this ratio increased by 10 to 18% when using 4% SBS and 3.5% PE, respectively. Fracture energy (area under the strength-strain curve) and elasticity were estimated for neat and modified mixture samples.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.