Effect of temperature on early-age properties of self-consolidating concrete equivalent mortar

In this study, the effect of material temperature during casting on fresh properties, hydration kinetics, and early-age compressive strength of self-consolidating concrete (SCC) was evaluated. Concrete equivalent mortars (CEMs) based on SCC mixture designs with water-to-binder ratios of 0.41 and 0.45 were investigated. The SCC mixtures are targeted for infrastructure and building construction and precast applications. The CEMs were prepared at temperatures ranging from 8 to 36°C.  Superplasticizer (SP) and air-entraining agent (AEA) demand were evaluated for the CEM mixtures made with different supplementary cementing material (SCM) and limestone filler types. Test results showed that the ambient temperature can significantly affect the SP and AEA demand, hydration kinetics, and compressive strength after 1 d of age. According to the ultraviolet–visible spectrophotometry (UV/Vis) test, the absorption rate of polycarboxylate-based SP decreased with temperature. In contrast, the sensitivity of polynaphthalene sulfonate-based SP to temperature was minimal. Relationships between the variations of different admixture contents, heat flux, and compressive strength with temperature were developed. For a constant slump flow and air content, the demand of the SP and AEA, heat flux, and 1-d compressive strength of CEMs increased linearly with material temperature.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.