Water Damage Resistance of Tuff Asphalt Mixtures with Admixtures Based on Surface Energy Theory

At present, tuff aggregates as asphalt pavement mixtures have insufficient water damage resistance; hence, modifying and evaluating the related properties of tuff asphalt mixtures are necessary. In this study, cement and a liquid antistripping agent were selected as admixtures, and tuff and limestone mixtures without admixtures were selected as control. The surface energy for the SBS-modified asphalt polymers and aggregates in the mixtures was evaluated by using surface energy theory. The adhesion work and the spalling work of the polymer–aggregate interface was calculated, and a factor k was proposed to predict the water damage resistance of the tuff mixture with admixtures. The prediction values were compared with those of the macroscopic water stability test for the mixture. The results of this research showed that the factor k after adding admixtures was improved, and the increase range was from 7.14% to 47.62%. The admixture scheme with the best improvement was that with 2% cement content, in which the k value increased by 21.57% and 47.62% compared with that of the limestone and tuff mixtures without admixtures, respectively. The tested water stability indexes and the predicted factor k under different admixture schemes exhibited a good positive correlation, and the correlation equations were obtained by linear fitting. Thus, it was feasible to use the factor k characterizing the water damage resistance of tuff mixtures using surface energy theory.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.