Ultrasonic measurement and elastic properties of the PbO-SrO-B2O3 glass system

Auteur(s):




Médium: article de revue
Langue(s): en 
Publié dans: Revista IBRACON de Estruturas e Materiais, , n. 4, v. 13
DOI: 10.1590/s1983-41952020000400015
Abstrait:

The PbO-SrO-B2O3 glass system with the of molar ratio of R (= PbO/B2O3) were prepared by fusion method. The elastic properties have been investigated using longitudinal and transversal ultrasonic wave velocity. Measurements were performed at room temperature and using pulse-echo technique at frequency of 5 MHz. The results indicate that, when increasing R value, the glass network stability decreases. This decrease indicates, of the increase the number of borate structures with non bridging oxygen (NBOs) at the expense of the decrease of borate units with tetrahedral structures. This feature may lead to the more open glass network structures and lower stiffness of the samples studied.

License:

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.

  • Informations
    sur cette fiche
  • Reference-ID
    10462061
  • Publié(e) le:
    25.10.2020
  • Modifié(e) le:
    25.10.2020