Test and Analysis of Concrete Beams Reinforced by Polyurethane Concrete–Prestressed Steel Wires (PUC–PSWs)

In order to solve the problems of low tensile strength of composite mortar prone to cracking when reinforced concrete beams are strengthened by traditional methods, this paper proposes a new polyurethane concrete–prestressing wire (PUC–PSW) reinforcement method using polyurethane concrete (PUC) as the wire embedding material. Twelve reinforced concrete T-beams were tested for PUC–PSW flexural reinforcement. These consisted of one unreinforced beam, four PSW-reinforced beams and seven PUC–PSW-reinforced beams. The wire embedding material, wire anchorage form, PUC material depth, amount of wire and loading type were used as variables. The test results show that PUC–PSW reinforcement can significantly increase the yield load and ultimate load of the reinforced beams by 24.1% and 44.6%, respectively, compared with PSW reinforcement. When the load reached 90 kN, the crack widths of PSW-reinforced beam A2 and PUC–PSW-reinforced beam A8 were 0.17 mm and 0.1 mm, respectively. The ability of PUC–PSW reinforcement to limit crack development is better than that of PSW reinforcement, especially after the main beam steel yield. The strength, stiffness and crack-limiting ability of the reinforced beam increase with the PUC thickness of the reinforced layer.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.