Sawdust Ash as Powder Material for Self-Compacting Concrete Containing Naphthalene Sulfonate

Tests are carried out to determine the fluidity of Ashaka Portland cement paste and its compatibility with sawdust ash (SDA) as powder material for self-compacting cement (SCC) mixtures. Results of the investigation showed that saturation was achieved at w/c ratios of 0.4 and 0.42, at dosages of naphthalene sulfonate superplasticizers of 3.5% and 2%, respectively. The optimum replacement level for the SCC mixture was 10 wt.% of cement by SDA and 2% of the superplasticizer dosage. The achieved spread and flow time were 26 cm and 8 seconds and are within the specified range of 24 cm to 26 cm and 7 to 11 seconds, respectively. Statistical inference showed that the mix, w/c, and the interaction between the mix and w/c ratio are significant.