Rheological and Strength Behavior of Binary Blended SCC Replacing Partial Fine Aggregate with Plastic E-Waste as High Impact Polystyrene

Disposing electronic plastic waste into construction materials is an eco-friendly and energy efficient solution to protect the environment. This work is aimed at enhancing the strength of self-compacting concrete (SCC) replacing sand with electronic waste, namely, High Impact polystyrene (HIPS) plastic granules and cementitious material with fly ash. SCC is designed with the optimized binder content of 497 kg/m³ using Fly Ash (30% by weight of cement) and 0.36 as water-to-binder ratio for all the mixtures. High Impact Polystyrene granules are replaced with sand up to 40% (by volume) at a regular interval of 10%. Rheological behavior is observed with the slump flow test for slump diameter, V-funnel test for flow time, and the L-box test for heights ratio, respectively. Strength behavior is studied by performing split tensile strength, and compressive strength tests after a period of 7, 28, and 90 days, respectively. Both fly ash and HIPS aggregate in addition to SCC up to 30% exhibits a minimal strength reduction with a promising performance in workability. Hence incorporation of both fly ash and HIPS granules up to 30% in SCC is a viable eco-friendly technique, with the beneficial economic impact on the construction industry.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.