Rehabilitation of Porous Building Components and Masonry by MICP Injection Method

Microbial-induced calcium carbonate precipitation (MICP) is a novel approach that is already being applied in various areas of construction. The precipitated calcium carbonate can be used to reduce porosity and thus increase the durability of deteriorated building components. This study investigates whether MICP injections are suitable for building rehabilitation. Porous mortar test samples of recycled aggregate and parts of deteriorated masonry were prepared. The MICP injections were performed without pressure and with an injection pump. The treatment effect was investigated after MICP injection by testing the porosity, strength and microscopic evaluation. It can be observed that multiple MICP injections under pressure result in a reduction of the pore volume of porous mortar samples. The produced calcium carbonate precipitates in the pore space of the samples and increases the density by 1.59% and the weight by 7.56%, which also results in a 48.3% reduction of the capillary water absorption. The results of strength tests show an increase of 45.16% in flexural strength and 35.64% in compressive strength compared with the untreated mortar samples. In addition, the MICP process was investigated and the precipitation was characterised. The X-ray diffraction (XRD) of the precipitated calcium carbonate confirms that mainly calcite was formed, which was also found in the pore structure of the MICP-injected masonry after the microscopic analysis. Precipitated calcium carbonate could be detected especially near the injection spots.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.