Recycling of Solar Panel Waste Glass as a Partial Replacement of Meta-kaolinite in the Production of Geopolymers

This investigation elucidates the mechanical characteristics of geopolymer containing solar panel waste glass. With the SiO₂/Na2O molar ratio (S/N = 0.75, 1.0, 1.25, 1.5, 1.75), the percentage of metakaolinite that is replaced by so-lar panel waste glass (0- 40%), and the curing time of 1, 7, and 28 days as the study variables, the porosity, density, setting time, compressive strength, and flexural strength of the geopolymer were evaluated. The morphology of geopolymer was examined using Scanning Electron Microscopy (SEM), and its microstructural properties were examined through Fourier transform infrared spectroscopy (FTIR) analysis. The results demonstrate that the S/N molar ratio significantly influences the mechanical and morphological characteristics of geopolymers. The geopolymer containing solar panel waste glass with an S/N of 1.75 had the greatest compressive strength. The intensity of the peak that represented Si-O-Al bonding of the geopolymer containing solar panel waste glass increased with the S/N. Analysis of the sample morphology revealed that the microstructures of stronger samples were more homogeneous and appeared denser. Furthermore, solar panel waste glass has the potential to partially replace metakaolinite as a geopolymer material, and to exhibit favorable me-chanical characteristics.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.