PH-monitoring in mortar with thermally-oxidized iridium electrodes

The pH of the concrete pore solution plays a vital role in protecting the reinforcing steel from corrosion. Here, we present results from embeddable pH sensors that permit the continuous, in-situ monitoring of the pH in the concrete pore solution. These are potentiometric sensors, based on thermally-oxidized iridium/iridium oxide (IrOx) electrodes. We propose an iterative calculation algorithm taking into account diffusion potentials arising from pH changes, thus permitting the reliable, non-destructive determination of the pore solution pH over time. This calculation algorithm forms an essential part of the method using IrOx electrodes. Mortar samples were exposed to accelerated carbonation and the pH was monitored at different depths over time. Comparative tests were also performed using thymolphthalein pH-indicator. The results from the pH sensors give insight in the carbonation process, and can, in contrast to thermodynamic modelling and titration experiments, give insight in kinetic processes such as transport and phases transformations. Additionally, it was found that the front at which the pH is decreased from initially 13-14 down to 12.5 can be significantly ahead of the common carbonation front corresponding to pH 9-10. This has major implications for laboratory testing and engineering practice.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.