Partial Replacement of Cement by Waste Paper Pulp Ash and Its Effect on Concrete Properties

An investigation was conducted to study the viability of using waste paper pulp ash as an alternative material applied as a partial replacement of cement in the manufacturing of concrete and its effect on the properties of concrete, and also, the cost and environmental advantage of using waste paper were examined. Four concrete mixes with 0%, 5%, 10%, and 15% waste paper pulp ash replacement of OPC and PPC for 25 MPa concrete were prepared. Based on the results obtained from the research, the highest compressive strength obtained at all test ages, i.e., 3, 7, and 28 days, were, 24.36, 28.35, and 36.83 MPa, respectively, with 5% replacement of waste paper pulp ash for OPC, and for PPC, all percentage replacements showed reduction in compressive strength than the control mix. The water absorption of concrete was increased with increasing the percentage of waste paper pulp ash than control concrete. The control concrete clearly has the lowest resistance to 2% sulfuric acid solution compared to blended concrete of OPC-WPPA and PPC-WPPA. The cost comparison indicates that the incorporation of waste paper pulp ash decreases the cost of concrete and WPPA and saves raw materials used in cement and concrete production.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.