On the use of the Jander equation in cement hydration modelling

The equation of Jander [W. Jander, Z. Anorg. Allg. Chem. (1927) 163: 1-30] is often used to describe the kinetics of dissolution of solid cement grains, as a component of mathematical descriptions of the broader cement hydration process. The Jander equation can be presented as kt/R2 =[1-(1-α) (1/3) ]2 where k is a constant, t is time, R is the initial radius of a solid reactant particle, and α is the fractional degree of reaction. This equation is attractive for its simplicity and apparently straightforward derivation. However, the derivation of the Jander equation involves an approximation related to neglect of particle surface curvature which means that it is strictly not correct for anything beyond a very small extent of reaction. This is well documented in the broader literature, but this information has not been effectively propagated to the field of cement science, which means that researchers are continuing to base models on this erroneous equation. It is recommended that if the assumptions of diffusion control and unchanging overall particle size which lead to the selection of the Jander equation are to be retained, it is preferable to instead use the Ginstling-Brounshtein equation [A.M. Ginstling, B.I. Brounshtein, J. Appl. Chem. USSR (1950) 23: 1327-1338], which does correctly account for particle surface curvature without significant extra mathematical complication. Otherwise, it is possible (and likely desirable) to move to more advanced descriptions of particle_fluid reactions to account for factors such as dimensional changes during reaction, and the possibility of rate controlling influences other than diffusion.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.