Martian Regolith Simulant-Based Geopolymers with Lithium Hydroxide Alkaline Activator

As humanity envisions the possibility of inhabiting Mars in the future, the imperative for survival in the face of its challenging conditions necessitates the construction of protective shelters to mitigate the effects of radiation exposure and the absence of atmospheric pressure. The feasibility of producing geopolymers using the Martian regolith simulant MGS-1 (as precursor) for potential building and infrastructure projects on Mars in the future is investigated in this paper. Various alkaline activators, such as sodium hydroxide (NaOH), lithium hydroxide (LiOH·H2O) and sodium silicate (Na2SiO3), are employed to investigate their efficiency in activating the precursor. The influence of alkali type and concentration on the mechanical performance of the synthesized geopolymers is examined. Geopolymer samples are oven-cured for 7 days at 70 °C before a compressive strength test. It is found that through the hybrid use of LiOH·H2O and NaOH with optimal concentrations, metakaolin and milled MGS-1 as precursors, geopolymer mixtures with a compressive strength of 30 ± 2 MPa can be developed. The present test results preliminarily demonstrate the potential of Martian regolith simulant-based geopolymers as suitable construction and building materials for use on Mars.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.