Laboratory and Full-Scale Testbed Study in the Feasibility of Styrene-Butadiene-Styrene Asphalt Pavement Having Epoxy Resin and Crumb Rubber Powder

Conventional asphalt concrete pavements have deteriorated rapidly due to the current increased traffic and extreme climate impacts. In addition to the upgrading in the construction quality, there is an urgent need to expand the utilization of modified asphalt binders to improve road capacity and traffic safety. The proposed research aims to combine epoxy resin (ER) and crumb rubber powder (CRP) contents into conventional Styrene-butadiene-styrene (SBS)-modified asphalt binder to not only reduce the consumption of normal asphalt binder but also promote the usage of recycled waste material in practice. To cope with this research objective, the ER and CRP were designed at 3% and 5% by weight of asphalt binder, respectively. Various laboratory tests were performed to evaluate the performance of modified mixtures (ERCRP), including the Frequency Sweep Test, Multiple Stressed Creep and Recovery, Dynamic Modulus, Semi-Circular Bending (SCB), and Cantabro Durability Tests. Additionally, an assessment of the modified asphalt concrete pavement via field testbed was conducted through Falling Weight Deflectometer and Ground Penetrating Radar. Overall, by adding the ER and CRP, the strain value of the control reference mix can be reduced up to 31.8% and 28.3% at MSCR 0.1 and 3.1 kPa, respectively. Additionally, the dynamic modulus of the ERCRP-modified samples was approximately 32,267 and 189 MPa, while the value of the reference mixture was 28,730 and 105 MPa at the highest and lowest frequency, respectively, indicating an enhancement under repeated loads. Regarding the SCB test results at 0 °C, the peak stress of the ERCRP-modified mixture was 4.75 MPa, while the value of the reference specimens was only 4.2 MPa, noticing the improved stress-bearing capacity. Based on a full-scale testbed, the FLWD elastic modulus of reinforced pavement shows a novel improvement (6.75%) compared with the control pavement, suggesting a potential application of ERCRP-modified asphalt binder for sustainable development purposes.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.