Investigation on the Impacts of Three Sea Salt Ions on the Performance of CSA-OPC Binary System

This study aimed to explore the impact of three corrosive ions—SO42−, Cl−, and Mg2+—on the hydration property of calcium sulphoaluminate (CSA) cement. Cement paste was prepared using three types of sea salt ion solutions with varying concentrations as mixing water. The experimental program encompassed assessments of porosity, compressive/flexural strength, heat of hydration, pH of pore solution, XRD, and SEM analysis. To modulate the hydration environment, Ordinary Portland cement (10%) was incorporated to elevate the pH and enhance the stability of ettringite, thereby facilitating the formation of additional C-S-H gel for the observation of M-S-H and other compounds. Findings revealed that the Cl− accelerated the hydration of CSA, resulting in heightened heat release. However, it also decreased the length-to-diameter ratio of ettringite, leading to cracking in CSA test blocks. The addition of SO42− resulted in elevated internal alkalinity, prompting alterations in hydration product types and subsequent reduction in CSA strength. Conversely, Mg2+ was observed to ameliorate the microstructure of CSA test blocks, diminishing porosity and augmenting strength.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.