The immediate and short-term degradation of the wood surface in a cement environment measured by AFM

This study aims to measure the pit torus and border to monitor the immediate and short_term degradation of wood surfaces after the concrete is cast and the cement hydration releases heat. The surface morphology and adhesion force curves were measured by atomic force microscopy during the treatments in saturated calcium hydroxide solutions ranging from 1 h to 27 days. The results showed that the pit torus and pit border showed different degradation processes. The adhesion force was sensitive to the type of the surface chemical components exposed during the degradation, while the surface modulus, deformation and jump-off force ratio were sensitive to the surface structural strength. The surface modulus of the pit torus degraded to 0.61–0.66 of the untreated original (95% CI) after 7-h treatments, and degraded almost completely after 48-h treatments. The surface modulus of the pit border degraded to 0.83–0.95 of the untreated original (CI) after 10 days and to 0.20–0.23 of the untreated original (95% CI) after 27 days of treatments. The treatment temperature 50 °C caused a 10-times faster degradation in the torus modulus compared to the temperature 20 °C.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.