Geopolymeric Composites Containing Industrial Waste Reinforced with Arundo donax Fibers

Traditional Portland cement-based composites have a great environmental impact. Alkali-activated binders can offer an alternative, particularly if they can be obtained even partially from waste. Two residuals derived from the finishing steps of the traditional ceramic industry have been used as possible polymerizable sources mixed with metakaolin. Moreover, to contrast the low dimensional stability of alkali-activated materials and their mechanical brittleness, natural fibers derived from the Arundo donax plant have been added to the mortars. The use of renewable natural fibers instead of synthetic ones can contribute a further environmental advantage. The fresh (consistency) and cured (mechanical) properties of composite materials prepared with residuals and metakaolin were analyzed here. For comparison’s sake, a reference set of composite materials not loaded with fibers but with an identical binder/sand and liquid/binder ratio was cast. A room-temperature curing condition was selected that, although inadequate to promote the short_time reactivity of the wastes, has a minimal energy requirement and allows on-site applications. A small-scale decrease in the properties in the compression mode tests was observed in the waste-modified mortars, while the Arundo addition improved their flexural strength and dimensional stability.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.