Evaluation of Methods to Correct the Effect of Temperature on Electrical Conductivity of Mortar

Nondestructive methods to obtain the electrical conductivity (σ) or resistivity (ρ) of concrete are gaining popularity for durability evaluation. However, these methods are susceptible to the effects of curing and conditioning, primarily temperature and degree of saturation. Beforeσof concrete at varied temperatures can be used for durability assessment, appropriate corrections must be made to account for the effect of temperature (T). In this study, two existing and one new temperature correction methods were evaluated for 12 mortar mixtures varying in water-to-cementitious material ratio (w/cm) and the content and types of supplementary cementitious materials (SCM). Mortar specimens instrumented with embedded sensors were cured in sealed conditions for 11–13 months. After this period, the sealed specimens were subjected to stepwise temperature change in 5–50°C range whileσwas recorded using the embedded sensors. Linear, bilinear, and Arrhenius temperature correction (LTC, BLTC, and ATC, respectively) were fitted to the obtainedσ-Tdatasets and were evaluated for fitness. LTC provided an acceptable fit to theσ-Tdata (R² > 0.81) but was found the most suitable in 5–30°C temperature range. BLTC was defined as a combination of two distinct LTC below and above the reference temperature at 23°C and had a better fit to the data (R² >0.96). Lastly, ATC showed the best fit among the tested methods (R² >0.98) and was found applicable for the full tested temperature range. Comparison of correction coefficients among the mixtures indicated that increase in w/cm results in less sensitivity ofσto temperature. Mixtures with SCM generally exhibit higher temperature sensitivity compared to the corresponding plain mixture. Since the variations in correction coefficients were not substantial (less 18% variation among 10 of 12 mixtures), a single value of activation energy of conduction (E_c) at 32 kJ/mol was identified as the general recommendation for all the tested mixtures.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.