Effects of GO/Al2O3 and Al2O3 Nanoparticles on Concrete Durability against High Temperature, Freeze-Thaw Cycles, and Acidic Environments

In this paper, the effect of GO/Al2O3 and Al2O3 synthesized nanoparticles on the durability of concrete is studied. To this end, after the synthesis of nanoparticles and confirmation of nanoparticles fabrication by SEM and FT-IR spectra, three concrete samples for each experiment related to each mix design were prepared and subjected to freeze-thaw cycles, high temperature, and acidic environment. The results show that the samples containing GO/Al2O3 nanoparticles had the least weight loss in freeze-thaw cycles as well as better resistance against acidic environment and the lowest apparent changes at high temperature compared to the samples containing nano-Al2O3 and the samples without nanoparticles. The replacement of 2 wt.% of cement with GO/Al2O3 nanoparticles results in the highest increase in concrete durability. The presence of nanoparticles in the concrete microstructure and the validation of the results are investigated by FT-IR, SEM, and EDX spectra.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.