Effect of Amount of Fibre and Damage Level on Service Life of SFR Recycled Concrete in Aggressive Environment

The paper presents a numerical calculation of the service life of concrete structures considering the effect of chlorides in the case of the material properties of structural lightweight waste aggregate concrete. Different amounts of fibres (0.0%, 1.0%, and 1.5%) and different values of compressive preloading (0%, 50%, and 100% of the ultimate strength capacity-USC) were considered. The subject of the research was the comparison of the influence of the constant diffusion coefficient and the time-dependent diffusion coefficient regarding the service life of the selected structure. Nine groups of material characteristics in combination with two numerical models are compared. A time-dependent diffusion coefficient and maturation coefficient, which were determined based on long-term monitoring (up to 461 days), were accepted for the numerical modelling. Thanks to time-dependent parameters, it is possible to observe the results of the theoretical service life of the structure and the influence of the mentioned factors. The analysed structure can be considered as the upper layer of an industrial floor in a chemical plant. It is important to determine the theoretical service life at which the structure shall be inspected or replaced. The results, in general, show that a higher amount of fibres reduces the service life as well as the preloading of the structure. An exception was a mixture with 1% of fibre loaded to 50% USC, which shows a lower diffusion coefficient than the specimens without preloading.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.