Cracking in Reinforced Concrete Structures Damaged by Artificial Corrosion: An Overview

Auteur(s):

Médium: article de revue
Langue(s): anglais
Publié dans: The Open Construction and Building Technology Journal, , n. 1, v. 13
Page(s): 199-213
DOI: 10.2174/1874836801913010199
Abstrait:

Background:

Corrosion of the reinforcing steel is a significant issue in construction engineering. As the corrosive attack propagates, the oxides accumulated on the steel-concrete interface cause a radial internal pressure in the structural element and induce a tensile stress state in the concrete with the consequent cracking. Except for few cases, the main outcomes on the behavior of reinforced concrete structures damaged by corrosion come from experimental results on artificially corroded specimens. For many years, the scientific community has been discussing the feasibility of artificial techniques to simulate the corrosion process in structural element. Specifically, the most disputed method is the accelerated electrolytic corrosion test, often characterized by high current intensities in order to reduce the duration of the experimental surveys.

Objective:

In the paper the influence of the current density on the degradation of a reinforced concrete element is investigated with particular reference to the kind of formed oxides and to the crack width.

Methods:

An experimental survey on steel rebars embedded in concrete cylinders and subjected to an electrolytic corrosion has been performed, with different increasing current densities. Furthermore, an analytical model, based on the classical thick-walled cylinder theory already proposed by the authors, is applied for validating the experimental results.

Results:

The oxides produced by artificial corrosion with different current densities are analyzed with X-ray diffractometry measurements. The influence of the current density on the crack widths is also pointed out.

Conclusion:

The analyses of the obtained results show that for the analysed specimens and current density range, no significant differences are found for the oxides composition. On the contrary the influence of the current density on the crack width is pointed out, and an upper limit of this parameter is indicated.

Copyright: © 2019 Stefania Imperatore, Zila Rinaldi
License:

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.

  • Informations
    sur cette fiche
  • Reference-ID
    10381020
  • Publié(e) le:
    22.11.2019
  • Modifié(e) le:
    02.06.2021