Complex Effect of Portland Cement Modified with Natural Zeolite and Ground Glass Mixture on Durability Properties of Concrete

This article analyses the combined effect of a mixture of natural zeolite and ground soda lime silicate glass on the durability properties of concrete. The specimens were prepared by replacing 25% of the cement with a mixture of zeolite and glass at different proportions with zeolite particles of two different sizes and cured for 28 and 90 days. Chloride migration, the depth of water penetration under pressure, and freeze–thaw cycle tests were performed, and compressive strength was determined. The combined effect of the mixture on the composition and microstructure of the cement matrix was studied by analysing the results of XRD, TGA, SEM-BSE, and porosity tests. The test results showed that irrespective of the cement “dilution” effect, the mixture of additives had a beneficial combined effect: increased durability of concrete, a denser structure of the cement matrix, the formation of calcium aluminate hydrates, faster rate, and higher degree of hydration.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.