Characterization of Mineralogical and Mechanical Parameters of Alkali-Activated Materials Based on Water Sediments Activated by Potassium Silicate

The circular economy transition encompasses the identification of various available and sustainable materials to replace traditional binders in the construction industry. The utilization of water sediments represents this point as a beneficial action that may provide synergy in terms of waste reduction and replacement of energy-intensive materials. To explore the potential of water sediments, this study contemplated the characterization of water sediments as precursors for the design of alkali-activated materials (AAMs). The experimental approach was based on the detailed characterization of raw materials’ chemical, mineralogical, and basic material properties and the assessment of the designed AAM paste and mortar samples. The results achieved revealed the capability of low amorphous water sediments to form dense structures with favorable mechanical performance, reaching up to 36.8 MPa in compressive strength. The microstructural and water sorption characteristics point to the applicability of such materials in the building practice and, thus, the valorization of water sediments into valuable material.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.