Axial Impact Resistance of High-Strength Engineering Geopolymer Composites: Effect of Polyethylene Fiber Content and Strain Rate

High-strength engineered geopolymer composite (EGC) materials exhibit excellent mechanical properties under quasistatic loading, thus showing great potential in military and civilian facilities subjected to impact or explosive loading. However, its dynamic mechanical response under high-speed loading is not fully understood. In this study, dynamic compressive test was performed on EGC with PE fiber contents of 0%, 0.5%, 1.0%, 1.5%, and 2.0% using the Split Hopkinson Pressure Bar (SHPB) test. The results indicated that EGC reinforced with 1.5% fiber exhibited optimal static and dynamic mechanical performance. In the strain rate range of 181 s−1 to 201 s−1, when the fiber content increased from 1.0% to 1.5% and 2.0%, the dynamic compressive strength of the EGC increased by 24.3%, 28.8%, and 44.0%, respectively, compared to the matrix without fiber. Dynamic parameters of the EGC, including dynamic compressive strength, dynamic increase factor, and impact toughness, showed sensitivity to strain rates and increased with strain rate. A modified model, incorporating the fiber bridging effect, was proposed based on the CEB-FIP model, providing important guidance for practical engineering applications.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.