Seismic Fragility Analysis of the Aging RC Columns under the Combined Action of Freeze–Thaw Cycles and Chloride-Induced Corrosion

The combined action of freeze–thaw cycles and chloride-induced corrosion are generally recognized as one of the main causes of the degradation of the mechanical properties and seismic performance of reinforced concrete (RC) structures in the northern frozen coastal regions. To investigate the degradation mechanisms of the seismic performance of RC columns subjected to the combined action of freeze–thaw cycles and chloride-induced corrosion, the impact of freeze–thaw cycles on the chloride diffusion coefficient of concrete was studied through concrete deterioration tests and theoretical analysis. This paper proposed a time-dependent deterioration model for RC columns, which is suitable to consider the combined action of freeze–thaw cycles and chloride-induced deterioration. The proposed deterioration model could be applied to the investigations of time-dependent seismic performance and the seismic fragility of RC columns. Based on the established deterioration model, this paper proposed a time-dependent seismic fragility analysis framework for the aging RC columns, considering the combined action of freeze–thaw cycles and chloride-induced corrosion. In addition, a representative three-span RC continuous T-shaped girder bridge that is located in the high-latitude northern frozen coastal regions of China was taken as the case study, and the time-dependent seismic fragility analysis of RC columns was conducted considering the involved uncertainties in geometric parameters, the deterioration mechanisms of the materials, and ground motions. The time-dependent seismic fragility curves of RC columns were obtained at different service time points. The results indicated that the combined action of freeze–thaw cycles and chloride-induced deterioration had a significant influence on the time-dependent seismic responses of the deteriorating RC columns. Under the combined action of freeze–thaw cycles and chloride-induced corrosion, when the RC bridge was in service for 75 years, the stirrup strength decreased by 3.88% and the cross-sectional area decreased by 30.03%. The peak stress of the confined concrete decreased by 52.1% and its peak strain increased by 12.2 times, respectively. Moreover, the time-dependent seismic fragilities of the aging RC columns under different damage states exhibited a nonlinear increase as the service life increased.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.