Mechanism on Activation of Coal Gangue Admixture

Coal gangue, an industrial waste, is rich in silicon and aluminum phase and may be used as a mineral admixture in concrete after moderately stimulating activity, allowing for efficient solid waste utilization. This study used a mortar strength and activity evaluation method to investigate single or compound activation methods to find the optimum activation method of coal gangue. FLIR, XRD, and SEM were used to investigate the activation mechanism of different modes, providing a theoretical foundation for the study of coal gangue as a concrete admixture. Results showed that mechanical ball milling, microwave, and chemical activator could activate coal gangue, and the composite activation effect was the best. The fineness of the coal gangue powder was more than 300 mesh, according to the optimal compounding method. Accordingly, the particle surface was smooth, the internal defects were reduced, and the microwave irradiation temperature was 700°C–800°C, causing the coal gangue particles to form a bonding surface and gradually agglutinate and densify. Meanwhile, the layered structure of kaolin minerals was destroyed, and a significant amount of glassy active SiO2 and Al2O3 was produced, enhancing the gel ability and activity of coal gangue. Finally, 8% Ca(OH)2 was added in the production of mortar specimens, which increased the alkalinity of the slurry, stimulated the rapid cracking and secondary hydration of the coal gangue, and enhanced the strength of mortar. At this time, the activity rate of coal gangue powder reached the highest, which was 90.5%.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.