Investigating the Calcination Temperature and Grinding Time of Calcined Clay on the Mechanical Properties and Durability of LC3 Concrete

Autor(en):


Medium: Fachartikel
Sprache(n): Englisch
Veröffentlicht in: Infrastructures, , n. 10, v. 8
Seite(n): 139
DOI: 10.3390/infrastructures8100139
Abstrakt:

The impact of the calcination temperature and grinding time on the mechanical properties and durability of limestone-calcined clay concrete (LC3) is crucial. In this research, calcined clay was produced within the temperature range of 700 °C to 900 °C, and the grinding time varied from 15 to 120 min. This study examines compressive strength and chloride penetration resistance using the rapid chloride migration test on LC3 concrete over a period of 180 days. The findings reveal that clay calcined at 800 °C for 120 min exhibited the highest specific surface area compared to other calcined clays. Furthermore, the compressive strength of LC3 concrete incorporating clay calcined at 800 °C for 60 min surpassed that of other mixtures investigated. Additionally, the chloride diffusion coefficient of LC3 concrete with calcined clay prepared at 800 °C for 120 min was lower than other mixtures.

Copyright: © 2023 the Authors. Licensee MDPI, Basel, Switzerland.
Lizenz:

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.

  • Über diese
    Datenseite
  • Reference-ID
    10746043
  • Veröffentlicht am:
    28.10.2023
  • Geändert am:
    07.02.2024
 
Structurae kooperiert mit
International Association for Bridge and Structural Engineering (IABSE)
e-mosty Magazine
e-BrIM Magazine