Impact of Blending on Strength Distribution of Ambient Cured Metakaolin and Palm Oil Fuel Ash Based Geopolymer Mortar

This paper investigates the influence of blending of metakaolin with silica rich palm oil fuel ash (POFA) on the strength distribution of geopolymer mortar. The broadness of strength distribution of quasi-brittle to brittle materials depends strongly on the existence of flaws such as voids, microcracks, and impurities in the material. Blending of materials containing alumina and silica with the objective of improving the performance of geopolymer makes comprehensive characterization necessary. The Weibull distribution is used to study the strength distribution and the reliability of geopolymer mortar specimens prepared from 100% metakaolin, 50% and 70% palm and cured under ambient condition. Mortar prisms and cubes were used to test the materials in flexure and compression, respectively, at 28 days and the results were analyzed using Weibull distribution. In flexure, Weibull modulus increased with POFA replacement, indicating reduced broadness of strength distribution from an increased homogeneity of the material. Modulus, however, decreased with increase in replacement of POFA in the specimens tested under compression. It is concluded that Weibull distribution is suitable for analyses of the blended geopolymer system. While porous microstructure is mainly responsible for flexural failure, heterogeneity of reaction relics is responsible for the compression failure.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 3.0 (CC-BY 3.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.