Exploration of Mechanisms of Joint Deterioration in Concrete Pavements regarding Interfacial Transition Zone

Autor(en):





Medium: Fachartikel
Sprache(n): Englisch
Veröffentlicht in: Advances in Civil Engineering, , v. 2018
Seite(n): 1-9
DOI: 10.1155/2018/3295954
Abstrakt:

As a common issue for cold weather regions, premature deterioration of concrete at joints has been reported in many states. In this paper, the mechanisms of joint deterioration were investigated, and then, experimental investigations were conducted to further verify some of the mechanisms. It was found that freeze-thaw (F-T) damage and salt crystallization are not enough to cause the observed deterioration, but the deterioration near the interfacial transition zone (ITZ) may be the cause of some of the observed phenomena. In the experimental work, samples were tested at 40°F in salt solutions to observe the deterioration in the ITZ using the scanning electron microscope (SEM). Concrete tested in MgCl2solution indicated distress in ITZ under SEM. It was found that ITZ may act as a shortcut for ion transfer to surrounding concrete near the joints and may also be the weak point for cracking due to expansion of the paste.

Copyright: © 2018 Xin Wang et al.
Lizenz:

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.

  • Über diese
    Datenseite
  • Reference-ID
    10222702
  • Veröffentlicht am:
    01.12.2018
  • Geändert am:
    02.06.2021
 
Structurae kooperiert mit
International Association for Bridge and Structural Engineering (IABSE)
e-mosty Magazine
e-BrIM Magazine