Effect of Nanosilica on Impermeability of Cement-Fly Ash System

Surface protection has been accepted as an effective way to improve the durability of concrete. In this study, nanosilica (NS) was used to improve the impermeability of cement-fly ash system and this kind of material was expected to be applied as surface protection material (SPM) for concrete. Binders composed of 70% cement and 30% fly ash (FA) were designed and nanosilica (NS, 0–4% of the binder) was added. Pore structure of the paste samples was evaluated by MIP and the fractal dimension of the pore structure was also discussed. Hydrates were investigated by XRD, SEM, and TG; the microstructure of hydrates was analyzed with SEM-EDS. The results showed that in the C-FA-NS system, NS accelerated the whole hydration of the cement-FA system. Cement hydration was accelerated by adding NS, and probably, the pozzolanic reaction of FA was slightly hastened because NS not only consumed calcium hydroxide by the pozzolanic reaction to induce the cement hydration but also acted as nucleation seed to induce the formation of C-S-H gel. NS obviously refined the pore structure, increased the complexity of the pore structure, and improved the microstructure, thereby significantly improving the impermeability of the cement-FA system. This kind of materials would be expected to be used as SPM; the interface performance between SPM and matrix, such as shrinkage and bond strength, and how to cast it onto the surface of matrix should be carefully considered.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.