A Comparative Analysis by Experimental Investigations on Normal and Ground Ultrafine Mineral Admixtures in Arresting Permeation in High-Strength Concrete

This paper discusses the permeation characteristics of concrete made by increasing the fineness of the conventional mineral admixtures and using them as a partial substitute for cement. Silica fume and metakaolin ground to ultrafine state and ceramic powder obtained from grinding waste ceramic tiles were used as mineral admixtures. The mixes were designed for a compressive strength of 50 MPa and were prepared for both binary and ternary blended cases. Binary blended specimens were cast, partially replacing cement with unground silica fume, ground silica fume, unground metakaolin, and ground metakaolin separately in different replacement proportions. Ternary blended mixes were prepared using ceramic powder in 4%, 9%, and 14% and with silica fume in a constant level of 1% percentage. All the cast specimens were compared against the control concrete. A deeper comparative analysis was also made by comparing the performance of specimens made with unground mineral admixtures with that of ground mineral admixtures. Various parameters such as resistance against water absorption, percentage of voids, and sorptivity characteristics were studied. It was observed that increasing the fineness helps fill up the pores, thereby improving the resistance to permeation action.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.