Spatial probabilistic analysis on a prestressed concrete slab bridge based on modified chloride diffusion coefficient model subject to chloride-induced corrosion

 Spatial probabilistic analysis on a prestressed concrete slab bridge based on modified chloride diffusion coefficient model subject to chloride-induced corrosion
Autor(en): , ,
Beitrag für IABSE Congress: Challenges in Design and Construction of an Innovative and Sustainable Built Environment, Stockholm, Sweden, 21-23 September 2016, veröffentlicht in , S. 439-446
DOI: 10.2749/stockholm.2016.0416
Preis: € 25,00 inkl. MwSt. als PDF-Dokument  
ZUM EINKAUFSWAGEN HINZUFÜGEN
Vorschau herunterladen (PDF-Datei) 0.19 MB

The performance of Prestressed Reinforced Concrete (PRC) structures degrades with time subject to chloride-induced corrosion. Corrosion could result in reduction of area of prestressing steel, cove...
Weiterlesen

Bibliografische Angaben

Autor(en): (School of Civil Engineering and Architecture, Changsha University of Science & Technology, Changsha, Hunan 410114, China)
(School of Civil Engineering and Architecture, Changsha University of Science & Technology, Changsha, Hunan 410114, China)
(School of Civil Engineering and Architecture, Changsha University of Science & Technology, Changsha, Hunan 410114, China)
Medium: Tagungsbeitrag
Sprache(n): Englisch
Tagung: IABSE Congress: Challenges in Design and Construction of an Innovative and Sustainable Built Environment, Stockholm, Sweden, 21-23 September 2016
Veröffentlicht in:
Seite(n): 439-446 Anzahl der Seiten (im PDF): 8
Seite(n): 439-446
Anzahl der Seiten (im PDF): 8
Jahr: 2016
DOI: 10.2749/stockholm.2016.0416
Abstrakt:

The performance of Prestressed Reinforced Concrete (PRC) structures degrades with time subject to chloride-induced corrosion. Corrosion could result in reduction of area of prestressing steel, cover cracking and even spalling due to corrosion products. This finally leads to a decrease of structural load-carrying capacity. Many factors influence corrosion induced by chloride ion, such as time, ambient humidity, temperature and loading. This paper proposes a modified chlorides diffusion coefficient model which considers the effect of time, ambient humidity, temperature and compressive stress. A spatial time-dependent reliability model is developed to predict probability of corrosion initiation over 100 years. Probabilistic evaluation of time to corrosion initiation has then been carried out for an aging PRC slab beam bridges exposed to aggressive environment. It is indicated that the probability of corrosion initiation for spatial variabilities considered with a scale of fluctuation of 3.0 is 1.06 times higher than that predicted for non-spatial. It is found that the probability of corrosion initiation for RH=90% is 12% higher than that predicted for RH=80%. It is also observed that a higher temperature will result in an increase in corrosion initiation probability. It is found from calculated results the spatial variability of parameters is important for reliability analysis.

Stichwörter:
Parameterstudie Tragwerkszuverlässigkeit