Performance of Zeolite-Based Soil–Geopolymer Mixtures for Geostructures under Eccentric Loading

Although soil stabilization with cement and lime is widely used to overcome the low shear strength of soft clay, which can cause severe damage to the infrastructures founded on such soils, such binders have severe impacts on the environment in terms of increasing emissions of carbon dioxide and the consumption of energy. Therefore, it is necessary to investigate soil improvement using sustainable materials such as byproducts or natural resources as alternatives to conventional binders—cement and lime. In this study, the combination of cement kiln dust as a byproduct and zeolite was used to produce an alkali-activated matrix. The results showed that the strength increased from 124 kPa for the untreated clay to 572 kPa for clay treated with 30% activated stabilizer agent (activated cement kiln dust). Moreover, incorporating zeolite as a partial replacement of the activated cement kiln dust increased the strength drastically to 960 and 2530 kPa for zeolite ratios of 0.1 and 0.6, respectively, which then decreased sharply to 1167 and 800 kPa with further increasing zeolite/pr to 0.8 and 1.0, respectively. The soil that was improved with the activated stabilizer agents was tested under footings subjected to eccentric loading. The results of large-scale loading tests showed clear improvements in terms of increasing the bearing capacity and decreasing the tilt of the footings. Also, a reduction occurred due to the eccentricity decreasing as a result of increasing the thickness of the treated soil layer beneath the footing.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.