Mechanical Properties of Fire-Damaged RC Beams Reinforced with Carbon Fiber Mesh

The bearing capacity of reinforced concrete (RC) beam will be weakened by fire. It is necessary to strengthen RC beams after fire. The carbon fiber mesh (CFM) can be used to reinforce RC beams. In this paper, RC beams were exposed to varying temperatures, followed by reinforcement with varying layers of CFM. The influence of the heating temperature and the number of CFM layers on the flexural performance of RC beams was investigated. The results indicated that the cracking loads of RC beams were 18.2, 16.4, 16.3, and 15.5 kN when the RC beams were subjected to room temperatures, 150, 350, and 550 °C. Compared to the unreinforced beams at room temperature, the cracking loads of the RC beams were reduced by 9.89%, 10.44%, and 14.84%. As the quantity of CFM reinforcement layers rises, so does the ultimate bearing capacity. For example, when the temperature was 150 °C, the ultimate loads of the beams with one and three layers of CFM were increased by 20% and 31.76% compared to the reference beam. When the temperature was 350 °C, the ultimate loads of the beams with one and three layers of CFM were increased by 19.51% and 28.04% compared to the RC beam without CFM. When the temperature was 550 °C, the ultimate loads of the beams with one and three layers of CFM were increased by 20% and 26.67% compared to the RC beam without CFM. Fire-damaged RC beams can be strengthened by one layer of CFM and mortar if the temperature was below 350 °C. Fire-damaged RC beams can be strengthened by three layers of CFM and mortar if the temperature was below 550 °C. The mechanical properties can be obviously enhanced.

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.