Investigation on the Corrosion of Coated Steel Plates with Impact Defect using Divided Steel Plates

Autor(en):



Medium: Fachartikel
Sprache(n): en 
Veröffentlicht in: Civil Engineering Journal, , n. 1, v. 4
Seite(n): 58
DOI: 10.28991/cej-030968
Abstrakt:

A method utilizing divided steel plates was used to investigate the corrosion of coated steel plates with impact defect while continuously submerged in 3% NaCl solution. The polarization behavior of circular divided steel plates was first compared to that of undivided ones. Half-cell potential and polarization resistance results show similar trend in divided and undivided form especially at the later stages of exposure. The method of using circular divided steel plates was then used to monitor the macrocell as well as microcell corrosion in coated steel plates induced with defect. The test results show that the defect causes macrocell corrosion to occur between the defect and sound portions. The impact defect also caused the reduction in the polarization resistance and consequently higher microcell corrosion at the neighbouring sound coated portions.

Copyright: © 2018 Marish S. Madlangbayan, Nobuaki Otsuki, Takahiro Nishida, Tsuyoshi Saito
Lizenz:

Dieses Werk wurde unter der Creative-Commons-Lizenz Namensnennung 4.0 International (CC-BY 4.0) veröffentlicht und darf unter den Lizenzbedinungen vervielfältigt, verbreitet, öffentlich zugänglich gemacht, sowie abgewandelt und bearbeitet werden. Dabei muss der Urheber bzw. Rechteinhaber genannt und die Lizenzbedingungen eingehalten werden.

  • Über diese
    Datenseite
  • Reference-ID
    10341076
  • Veröffentlicht am:
    14.08.2019
  • Geändert am:
    14.08.2019